In Situ High-Temperature Raman Spectroscopy of UCl3: A Combined Experimental and Theoretical Study.

Uranium trichloride (UCl3) has received growing interest for its use in uranium-fueled molten salt reactors and in the pyrochemical processing of used fuel. In this paper, we report for the first time the experimentally determined Raman spectra of UCl3, at both ambient condition and in situ high temperatures up to 871 K. The frequencies of five of the Raman-active vibrational modes (vi) of UCl3 exhibit a negative temperature derivative ((∂νi/∂T)P) with increasing temperature. This red-shift behavior is likely due to the elongation of U-Cl bonds. The average isobaric mode Grüneisen parameter (γiP = 0.91 ± 0.02) of UCl3 was determined through use of the coefficient of thermal expansion published in Vogel et al. (2021) and the (∂νi/∂T)P values determined in this study. These results are in general agreement with those calculated here by density functional theory (DFT+U). Finally, a comparison of the ambient band positions of UCl3 to those of isostructural lanthanide (La-Eu) and actinide chlorides (Am-Cf) has been made.

Sample seal-and-drop device and methodology for high temperature oxide melt solution calorimetric measurements of PuO2.

Thermodynamic properties of refractory materials, such as standard enthalpy of formation, heat content, and enthalpy of reaction, can be measured by high temperature calorimetry. In such experiments, a small sample pellet is dropped from room temperature into a calorimeter operating at high temperature (often 700 °C) with or without a molten salt solvent present in an inert crucible in the calorimeter chamber. However, for hazardous (radioactive, toxic, etc.) and/or air-sensitive (hygroscopic, sensitive to oxygen, pyrophoric, etc.) samples, it is necessary to utilize a sealed device to encapsulate and isolate the samples, crucibles, and solvent under a controlled atmosphere in order to prevent the materials from reactions and/or protect the personnel from hazardous exposure during the calorimetric experiments. We have developed a sample seal-and-drop device (calorimetric dropper) that can be readily installed onto the dropping tube of a calorimeter such as the Setaram AlexSYS Calvet-type high temperature calorimeter to fulfill two functions: (i) load hazardous or air-sensitive samples in an air-tight, sealed container and (ii) drop the samples into the calorimeter chamber using an "off-then-on" mechanism. As a case study, we used the calorimetric dropper for measurements of the enthalpy of drop solution of PuO2 in molten sodium molybdate (3Na2O·4MoO3) solvent at 700 °C. The obtained enthalpy of -52.21 ± 3.68 kJ/mol is consistent with the energetic systematics of other actinide oxides (UO2, ThO2, and NpO2). This capability has thus laid the foundation for thermodynamic studies of other Pu-bearing phases in the future.

The valence-fluctuating ground state of plutonium.

A central issue in material science is to obtain understanding of the electronic correlations that control complex materials. Such electronic correlations frequently arise because of the competition of localized and itinerant electronic degrees of freedom. Although the respective limits of well-localized or entirely itinerant ground states are well understood, the intermediate regime that controls the functional properties of complex materials continues to challenge theoretical understanding. We have used neutron spectroscopy to investigate plutonium, which is a prototypical material at the brink between bonding and nonbonding configurations. Our study reveals that the ground state of plutonium is governed by valence fluctuations, that is, a quantum mechanical superposition of localized and itinerant electronic configurations as recently predicted by dynamical mean field theory. Our results not only resolve the long-standing controversy between experiment and theory on plutonium's magnetism but also suggest an improved understanding of the effects of such electronic dichotomy in complex materials.